Synthetic Rubber SBR 1712

General

Polymer Properties	Minimum	Maximum	Method
Volatile Matter, %		0.60	GB/T 24131-2009
Tro, %		0.50	GB/T 4498-1997
Organic Acid, %	3.90	5.70	GB/T 8657-2000
Soap %	—	0.50	GB/T 8657-2000
(Dầu), %	25.3	29.3	SH/t 1718-2000
Bound Styrene, %	22.3	24.5	GB/T8658-1998
Mooney Viscosity, 50ml (1 + 4)100 ℃	44	54	GB/T 1232.1-2000

Properties of vulcanized rubber compound at 145 ℃ GB/T 8656-1998 A

Compound, 50ml (1 + 4)100 ℃		70	GB/T 1232.1-2000
Tensile Strength, MPA, 35 minutes	19.4		GB/T 1232.1-2000 GB/T 528-2009
Elongation, %, 35 minutes	380		GB/T 1232.1-2000 GB/T 528-2009
Modulus, MPA (25 minutes)	9.8	13.8	GB/T 1232.1-2000 GB/T 528-2009
Modulus, MPA (35 minutes)	12.1	16.1	GB/T 1232.1-2000 GB/T 528-2009
Modulus, MPA (50 minutes)	13.1	17.0	GB/T 1232.1-2000 GB/T 528-2009

Packaging

Sealed with PE film and packed in kraft bags lined with IDPE, or MB5 cartons for rubber bales, with a net weight of (35.0 ± 0.5) kg/bag.